How to judge BGA with X-Ray?

2019-03-27

How to judge BGA by X-Ray?


三分时时彩计划 Ailant SMT Test Series:

20170630113199479947.png



三分时时彩计划 Standard BGA:

20170630105359575957.png


1, image 1, 2 at the joint tin, the reason analysis: there is a problem in the printing solder paste, need to detect the printing link;

三分时时彩计划 2, image 3, there is a jagged shape around the solder ball, the reason analysis: the tin is not enough or the furnace temperature reflow time is short,

三分时时彩计划 Most of this will appear as a phenomenon of soldering;

3, image 4, the solder paste is not uniform, the reflow time is too short, and most of this is a phenomenon of soldering.

20170630105973447344.png





1, the figure 1, 2 Shaoxi, most of the printing links are less printed, it may be the ball;

2, Figure 3, 4 voids, voids The current IPC standard is that the void area cannot exceed 25% of the tin sphere. There are many reasons for the formation of voids.

   In particular, the current lead-free process basically has voids, and the root cause of void formation is the melting point of most solder pastes in solder paste.

   Too high to be volatilized in time to form a residue. Too large a void area can affect the reliability of the solder joint.


20170630110590759075.png

1, Figure 1 oblique image, this board has multiple defects: even tin, less ball, less tin, etc., this board should be a rework board;

2, there are many holes and drifts in Figure 2;

3, Figure 3, 4 solder is not completely molten, that is, cold welding. Most of these are lead-free processes, which should have a higher lead-free melting point and poor wettability.

三分时时彩计划    It is more difficult to control the reflow time or temperature in the reflow furnace.

20170630110953525352.png

三分时时彩计划 1, Figure 1 less tin ball, Figure 2 Shaoxi may be a virtual weld. Most of this phenomenon is a problem when printing;

三分时时彩计划 2, Figure 3, 4 is Flip chip, the figure appears multiple failures, less balls, even tin, multiple tin, hollow. The image should be the board after the repair.

三分时时彩计划     Figure 4 shows multiple times of tin, for the same reason as Figure 3.

20170630111492149214.png

三分时时彩计划 1, Figure 1 is whitish compared to Figure 2, significantly less tin, may not print unevenly;

三分时时彩计划 2, Figure 3, 4 pins are a bit biased, may be misaligned when mounting;

3, Figure 5 bit PLCC shows open circuit, no pin;

4, there are holes in many places in Figure 6, Figure 7 shows a phenomenon of drift, there may be no solder oil here.


National Service Hotline

400-630-6556

Shenzhen Ailant Technology Co., Ltd. All rights reserved

三分时时彩计划 Address: 3rd Floor, Building B, Building 3, Building 2, Guangshen Road, Chaogang Town, Songgang Town, Bao'an District, Shenzhen, China.

Tel: 0755-29411968

三分时时彩计划 Fax: 0755-27330185

三分时时彩计划 E-mail :elt@elt-usa.com

Website: Http://365boxstv.com

粤ICP备14073693号

Hong Kong Ai Te Te Electronic Technology Co., Ltd.
Address: 16th Floor, Zhuo Neng Century Plaza, 250 Hennessy Road, Wanchai, Hong Kong.
Tel: 00852-25755186
Fax: 00852-28911996

Aitech Electronic Technology (Suzhou) Office
Address: Xiangcheng Economy, Suzhou City Room 1203, East Xinxin International Building, No. 2 Jiayuan Road, Development Zone
Tel: 0512-69578096
Fax: 0512-68380859
Mobile: 18915434123
E-mail: qilong6868@elt-usa.com
  • Wechat Public Number

  • Mobile website

一分时时彩计划人工 五分时时彩官网 PK10注册送28网站 PK10官网开奖直播 加拿大28-加拿大28投注平台 CP9368 PK10官网开奖直播 北京pk10_北京pk10官网_北京pk10开奖官网 三分时时彩_三分时时彩是哪开的_三分时时彩预测计划 欢乐生肖平台 北京赛车pk10官网-北京赛车pk10计划_北京赛车pk10开奖 Toyou